VELVET

Plate thickness 6cm periphery of the central part thickness and 12mm 800kg ciment/m3 dosed concrete and limestone, adjuvant water reducer superplasticizer.

Concrete 2% of glass fiber / steel bar periphery of the plate.

Dye-based iron oxide integrated mixing.

By glazed finish polyurethane varnish and wax white surface.

The tray resting on a metal frame composed of square tubes of 40mm. 4 feet by a triangular central truss T steel, all bolted to the upper frame.

NUDE

Tray 3 cm thick composed of PBA: finely developed coating cement, silica, marble powder and epoxy resin.

Staining pigments of iron oxide on chipboard.

Two component polyurethane resin vitrification.

Jamb: idem.

ALMA

Plate thickness of 1.5 cm.

Dosed at 800kg concrete and calcium-silicate ciment/m3, adjuvant superplasticizer water reducing.

Concrete 2% of glass fiber.

Dye-based iron oxide integrated mixing.

By glazed finish polyurethane varnish and wax white surface.

NOVA

Plate thickness 6cm periphery and central recess polystyrene.

Dosed at 800kg concrete and calcium-silicate ciment/m3, adjuvant superplasticizer water reducing.

Concrete 2% of glass fiber and steel rods on either side of the tray.

Dye-based iron oxide integrated mixing.

By glazed finish polyurethane varnish and wax white surface.

Leg compound identical to the plate of concrete.

Central core of polystyrene, high and low felt.

LORETA

Plate thickness 13cm composed of PBA:

coated finely developed cement, silica, marble powder and epoxy resin.

Staining pigments of iron oxide on chipboard.

Two component polyurethane resin vitrification.

Jamb: idem.

GAIA

Plate thickness 3cm.

Dosed at 800kg concrete and calcium-silicate ciment/m3, adjuvant superplasticizer water reducing.

Concrete 2% of glass fiber.

Dye-based iron oxide integrated mixing.

By glazed finish polyurethane varnish and wax white surface.

4 feet perforated metal, laser cutting.

Bespoke dimensions possible.